6061 vs 6082: which aluminium alloy is better?
Strength, extrudability, anodising and uses of alloys 6061 and 6082, side by side and with the values from the standard.
In a nutshell
- 6082 is stronger: 290 MPa tensile strength against 260 MPa, and 250 against 240 MPa yield strength.
- Both weld equally well (4 out of 5); as with any heat-treated alloy, the weld zone loses some of its strength.
| Property | 6061 | 6082 |
|---|---|---|
| Tensile strength (Rm) | 260 MPa | 290 MPa |
| Yield strength (Rp0.2) | 240 MPa | 250 MPa |
| Elongation (A) | 8% | 8% |
| Approximate hardness | 95 HB | 95 HB |
| Density | 2.70 g/cm³ | 2.70 g/cm³ |
| Composition | Si 0.40–0.80 · Mg 0.80–1.20 · Cu 0.15–0.40 · Cr 0.04–0.35 | Si 0.70–1.30 · Mg 0.60–1.20 · Mn 0.40–1.00 |
| Extrudability (1 to 5) | 3 | 3 |
| Decorative anodising (1 to 5) | 3 | 3 |
| Weldability (1 to 5) | 4 | 4 |
| Corrosion resistance (1 to 5) | 4 | 4 |
| Machinability (1 to 5) | 4 | 4 |
Values in T6 temper: minimums from the EN 755-2 standard for thin-walled profiles (they vary with thickness and shape). Approximate hardness. The 1 to 5 ratings compare these alloys with each other.
- Choose 6061Structural and machined parts, marine, bicycles, brackets, flanges and machine components.
- Choose 6082The strongest of the 6000 series: structures, bridges, cranes, scaffolding, trailers and highly stressed parts.
Still not sure which to use?
Tell us what you are going to make and we will recommend the right alloy, temper and finish.
The message is put together with what you are looking at, with no obligation.
Frequently asked questions
Which is stronger, 6061 or 6082?
6082: in T6 temper it has a minimum tensile strength of 290 MPa, against 260 MPa for 6061 (EN 755-2 standard, thin-walled profiles).
What are 6061 and 6082 used for?
6061: structural and machined parts, marine, bicycles, brackets, flanges and machine components. 6082: the strongest of the 6000 series: structures, bridges, cranes, scaffolding, trailers and highly stressed parts.
Which one is better for anodising?
Both anodise equally well (3 out of 5).